Type: | Welding Wire |
---|---|
Material: | Carbon Steel |
Flux Containing: | Not Containing Flux |
Slag Characteristic: | Acidic |
Extended Length: | 10-20mm |
OEM & ODM: | Accepted |
Customization: |
---|
Suppliers with verified business licenses
Weifang Forward Welding Materials Co., Ltd. | ||
Sales MIG Welding Wire and Submerged Arc Welding Wire |
Honors | the member of China Iron & Steel Association | ||
China Chamber of Commerce of Metals Minerals & Chemicals Imp. & Exp. | |||
top 500 enterprises in manufacture industry of China | |||
top 100 enterprises in Shandong Province | |||
top 10 enterprises in Weifang City |
Product Name: | MIG welding wire | ||
Grade: | AWS A5.18 ER70S-6 | ||
GB/T ER50-6 | |||
Certificate: | CCS, ABS, DNV, NK, LR, BV, GL, KR, CWB, BKI and etc. |
Available Size | Package1 | Package2 | Package3 |
0.8mm | 5kg/D200 Plastic Spool | 15kg/D270 Plastic Spool | / |
0.9mm | 5kg/D200 Plastic Spool | 15kg/D270 Plastic Spool | / |
1.0mm | 5kg/D200 Plastic Spool | 15kg/D270 Plastic Spool | 250kg/pail |
1.2mm | / | 15kg/D270 Plastic Spool | 250kg/pail |
1.6mm | / | 15kg/D270 Plastic Spool | 250kg/pail |
N.W. 5kg Package | 5kg/D200 plastic spool, 5.6kg/box, 200boxes/pallet, 24pallets/1x20'GP | ||
N.W. 15kg Package | 15kg/D270 plastic spool, 16kg/box, 72boxes/pallet, 24pallets/1x20'GP | ||
N.W. 250kg Package | 250kg/pail,4pails/pallet, 22pallets/1x20'GP |
Standards and steel grade | GB | ER50-6 |
AWS | ER70S-6 | |
Specificationφ(mm) | 0.8-1.6 | |
Welding wire chemical composition | C | 0.06-0.15 |
Mn | 1.40-1.85 | |
Si | 0.80-1.15 | |
P | ≤0.025 | |
S | ≤0.035 | |
Cr | - | |
Ni | - | |
Cu | ≤0.50 | |
Mechanical Properties of deposited metal | σs(MPa) | ≥420 |
σb(Mpa) | ≥500 | |
σ5(%) | ≥22 | |
AKV J(ºC) | ≥27(-29) | |
Shielded Gas | CO2 | |
Main Applications | For welding low carbon and high strength steel structures of 500MPa |
Important Tips | 1. Remove the rust, oil, moisture and other impurities from base metal. | ||
2. Welding heat input will directly affect the mechanical perties of welds. | |||
2-1. Welding heat input depends on the importance of struture. | |||
2-2. The more important the structure is, the smaller the welding heat input |